Alternative Title: Effect of Forging Condition on the Microstructure and Mechanical Properties of Centrifugal Casted Heat Resistant Steel

Abstract: The aim of this study is investigated to develop the optimum forging conditions on B7B4 heat resistant steel.
The results obtained from this study are as follow.
With increasing forging start temperature, tensile strength increased, but hardness and elongation presented decreasing tendency.
The volume fraction of ferrite structure increased with increasing forging start temperature. With increasing forging rate, tensile strength, hardness and impact value increased, but elongation decreased. With forging finish temperature, tensile strength and impact value increased, but hardness and elongation decreased. Also, the volume fraction for ferrite increased with forging finish temperature.

URI: https://repository.pknu.ac.kr:8443/handle/2021.oak/11116
http://pknu.dcollection.net/jsp/common/DcLoOrgPer.jsp?sItemId=000001955552

Table Of Contents: 1. 서론 = 1
2. 이론적 배경 = 3
2-1. 9~12%Cr강에서의 미세조직 = 3
2-2. 9~12%Cr계 합금의 종류 = 3
2-2-1. 초기의 9~12%Cr 합금 = 4
2-2-2. 화력발전소 보일러용 9~12%Cr 합금 = 4
2-2-2-1. Conventional 9~12%Cr 합금 = 4
2-2-2-2. Advanced 9~12%Cr 합금 = 5
2-2-3. 터빈 로터용 9~12%Cr 합금 = 9
2-2-3-1. Conventional 9~12%Cr 합금 = 11
2-2-3-2. Advanced 9~12%Cr 합금 = 11
2-3. 석출상의 종류 = 15
3. 실험방법 = 18
3-1. 시료 = 18
3-2. 단조조건 변화 = 18
3-3. 미세조직 관찰 = 20
3-4. 기계적 성질 = 20
4. 실험결과 및 고찰 = 21
4-1. 미세조직 및 기계적 성질에 미치는 단조 시작 온도의 영향 = 21
4-1-1. 미세조직변화에 미치는 단조 시작온도의 영향 = 21
4-1-2. 기계적 성질 변화에 미치는 단조 시작 온도의 영향 = 24
4-2. 미세조직 및 기계적 성질에 미치는 단조 마무리 온도의 영향 = 31
4-2-1. 단조 마무리 온도 따른 미세조직관찰 = 31
4-2-2. 기계적 성질에 미치는 단조 마무리 온도의 영향 = 35
4-3. 미세조직 및 기계적 성질에 미치는 단조비의 영향 = 41
4-3-1. 단조 비 변화에 따른 미세조직관찰 = 41
4-3-2. 단조 비 변화에 따른 기계적 성질 변화 = 45
5. 결론 = 52
참고문헌 = 53