PEDOT:PSS-C 상대전극 제작에 따른 DSSC의 효율 특성
- Abstract
- Counter electrode is an important component for DSSC , this research on it . Through the method of adding different amount of DMSO and charcoal activated, the PEDOT:PSS-C electrical characteristic and efficiencies of DSSCs with photo electrode surface area were studied . In the case of not adding any reagent , the highest short circuit current density of PEDOT: PSS was 11.480mA/c㎡. Through adding DMSO , It would be change PEDOT:PSS on basal ITO/ PEN adhesion . When PEDOT:PSS DMSO is2：1， the highest current density is 13.720 mA/c㎡, the best efficiency shows 4.208%. When adding 0.1wt% of charcoal activated , the highest efficiency is 4.744% .
- Issued Date
- 2015
- Awarded Date
- 2015. 8
- Type
- Dissertation
- Publisher
- 부경대학교
- Alternative Author(s)
- LIU XIAOPING
- Affiliation
- 부경대학교
- Department
- 대학원 전기공학과
- Advisor
- 권성열
- Table Of Contents
- Ⅰ. 서 론 1
Ⅱ. 이론적 배경 3
1. 태양전지의 월리와 종류 3
가. 태양전지의 기본원리 3
나. 태양전지의 종류 4
2. 태양전지의 특성평가 6
가. 광전효과 6
나. I-V curve 9
다. Air mass 12
3. 염료감응형 태양전지 14
가. DSSC 개요 14
나. DSSC의 구조 15
다. DSSC의 구성 16
라. DSSC의 동작원리 19
Ⅲ. DSSC 제작 21
1. DSSC 제작공정 21
가. 광전극 제작 21
나. 상대전극 제작 22
다. 두 기판 결합 22
2. DMSO 첨가량에 따른 DSSC 제작 24
3. 활성탄첨가량에 따른 DSSC 제작 25
4 특성 평가 26
Ⅳ. 결과 및 고찰 28
1. DMSO 첨가량에 따른 DSSC 측정결과 28
2. 활성탄첨가량에 따른 DSSC 측정결과 32
3. PEDOT:PSS-C 첨가에 따른 DSSC 측정결과 36
Ⅴ. 결 론 40
참고문헌 42
- Degree
- Master
- Files in This Item:
-
-
Download
PEDOT:PSS-C 상대전극 제작에 따른 DSSC의 효율 특성.pdf
기타 데이터 / 2.65 MB / Adobe PDF
-
Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.