친환경 water-borne 무기징크 도료 개발 및 성능평가
- Abstract
- The water-borne inorganic zinc-rich was developed by using the alkali silicate not the alkyl silicate in order to limit the content of the volatile organic compounds of the paint. By mixing the Zn power by the content of wt%, the property evaluation of the film was engaged in after the painting. The following were engaged in: The SEM-EDS analysis, the adhesive test, and the evaluation of the environmental friendliness. Also, in order to confirm the special characteristics of the cathodic protection according to the Zn powder content, the Salt Spray Test was conducted. And the open circuit potential measurement for the quantitative evaluation was carried out.
- Issued Date
- 2015
- Awarded Date
- 2015. 8
- Type
- Dissertation
- Publisher
- 부경대학교 대학원
- Affiliation
- 부경대학교 대학원
- Department
- 대학원 공업화학과
- Advisor
- 박진환
- Table Of Contents
- 1. 서론 1
2. 이론적 배경 3
2.1 아연말 도료의 개요 3
2.2 무기질 아연말 도료의 분류 4
2.2.1 Post-curing, water-borne 6
2.2.2 Self-curing, water-borne 7
2.2.3 Self-curing, solvent-borne 8
2.3 음극보호(Cathodic protection) 11
2.4 휘발성 유기화합물 13
2.4.1 휘발성 유기화합물의 정의 13
2.4.2 국가별 휘발성 유기화합물 규제동향 14
2.4.3 도료 내 VOCs 함량분석방법 18
3. 실험방법 19
3.1 Water-borne 무기징크 도료 제조 19
3.2 시험편 제작 21
3.3 주사전자현미경 분석 22
3.4 도료의 친환경성 평가 23
3.5 도막의 부착력 시험 25
3.6 도막의 방식성능 평가 27
3.6.1 가속노화시험 27
3.6.2 개회로 전위 측정 28
4. 결과 및 고찰 30
4.1 Water-borne 무기징크 도료 30
4.2 아연안료 함량에 따른 도막의 SEM-EDS 비교 31
4.3 도료의 친환경성 평가 35
4.4 도막의 부착력 측정 37
4.5 도막의 방식성능 평가 40
4.5.1 염수분무시험에 따른 아연함량별 도막의 내식성 40
4.5.2 아연함량별 도막의 개회로 전위 변화 45
5. 결론 51
Reference 53