Abstract: Zinc are widely used to control the corrosion of metal. so this thesis study
deep into a zinc particle.
Zinc particle were tested on SEM-EDS and FE-SEM. First, zinc particle were immersed in distilled water during 20days. Second, another zinc partice were immersed in distilled water and 5% NaCl solution during 30days.
After 300h in distilled water, a zinc particle seems like white rusts. 5% NaCl solution`s oxidation rate is faster than distilled water. Because chemical potential is different between distilled water and 5% NaCl. zinc`s corrosion product is variable and function as protective film.

Keyword: zinc zinc particle sem-eds fe-sem white rust oxidation rate chemical potential.

URI: https://repository.pknu.ac.kr:8443/handle/2021.oak/13013
http://pknu.dcollection.net/jsp/common/DcLoOrgPer.jsp?sItemId=000002235598

Table Of Contents: 1. 서론 1
2. 이론적 배경 3
2.1 아연의 개요 3
2.1.1 아연의 역사 3
2.1.2 아연의 발생 4
2.1.3 아연의 광상 4
2.1.4 아연 광물 5
2.1.5 아연의 생산 _ 광석으로부터 금속 아연광 5
2.1.6 아연 용도 7
2.1.7 아연의 지속성 7
2.1.8 도장 10
2.1.9 아연 도금 유형 12
2.1.10 제품유형 14
2.1.9 일반적인 아연 도금 15
2.2 안료 20
2.2.1 안료의 정의 20
2.2.2 안료의 역할 20
2.2.3 안료의 요구 물성 20
2.2.4 안료의 분류 21
2.2.5 안료의 성질 24
2.2.6 안료의 종류별 특성 28
2.3 유기 도막의 방식 특성 31
2.4 음극방식 34
3. 실험방법 37
3.1 시험편 제작 37
3.2 가속노화시험 38
3.2.1 염수분무시험 38
3.2.2 증류수 노출시험 38
3.3 주사전자현미경 분석 39
3.4 Auriga CrossBeam 40
4. 결과 및 고찰 43
4.1. 아연 입자 증류수 침지시간에 따른 SEM 비교 43
4.2 아연 입자 증류수 침지 후 시간에 따른 FIB- Cross section 관찰 46
4.3 아연 입자 0.5M NaCl 용액에 침지 후 시간에 따른 FIB-Cross section 관찰 53
5. 결론 61
Reference 62

Authorize & License

qrcode