PUKYONG Repository 대학원 금속공학과

Metadata Downloads

Abstract: Aluminum alloy have been used various fields such as mobile due to its high strength, thermal conductivity and lightness. However, high reactivity of aluminum alloy causes corrosion problem. Anodic oxidation (or anodizing) is one of effective method that creates passive layer on aluminum to improve corrosion resistance. Anodizing makes nanoporous oxide on the surface, so it should be sealed because they provide paths of corrosive media into aluminum substrate. High temperature sealing high energy consumption and expensive to maintain solution temperature. Low temperature sealing such as Nickel fluoride has a long processing time and low solubility. In this study, we designed a new solution for low temperature sealing treatment includes ammonium based materials and nickel based materials. Nickel and fluorine ion spices make hydroxide and fluoride during sealing. With the concentration of solution, sealing treatment time reduced to minimize the corrosion current density of aluminum alloy. MNFS 2 showed better corrosion resistance than traditional cold sealing and hot sealing.

URI: https://repository.pknu.ac.kr:8443/handle/2021.oak/2336
http://pknu.dcollection.net/common/orgView/200000368669

Table Of Contents: 1. 서 론 1
2. 이론적 배경 4
2.1 전기화학 이론 4
2.1.1 전기화학적 포텐셜 4
2.1.2 전기화학반응 속도 8
2.2 알루미늄 합금 12
2.2.1 알루미늄 합금의 종류 및 활용 12
2.2.2 알루미늄의 부식 15
2.3 알루미늄 양극 산화 19
2.3.1 알루미늄 양극 산화 원리 19
2.3.2 알루미늄 양극 산화 종류 23
2.4 봉공 처리 26
2.4.1 고온 봉공 처리 26
2.4.2 저온 봉공 처리 28
3. 실험 방법 29
3.1 실험 개요 29
3.2 시편 전처리 30
3.3 양극 산화 30
3.4 봉공 처리의 영향 31
3.5 내식성 평가 32
4. 실험결과 및 고찰 36
4.1 양극 산화 피막의 형상 및 내식성 36
4.2 봉공 처리가 피막 내식성에 끼치는 영향 40
4.2.1 기존 봉공 처리법에 의한 표면 형상 변화 40
4.2.2 처리 시간에 따른 내식성의 변화 44
4.3 혼합 용액을 이용한 봉공 처리의 영향 48
4.3.1 이온 농도에 따른 표면 형상 변화 48
4.3.2 이온 농도 및 처리 시간이 내식성에 끼치는 영향 54
4.3.3 혼합 용액 종류에 따른 내식성 61
5. 결론 68
참고 문헌 72