가공열처리한 Fe-20Mn-12Cr-3Ni-3Si 합금의 강도와 감쇠능의 상호관계
- Alternative Title
- The Corelationship between Strength and Damping Capacity of Thermo-mechanical Treated Fe-20Mn-12Cr-3Ni-3Si Alloy
- Abstract
- This study was processed to investigate the co-relationship between the mechanical properties and damping capacity of thermo-mechanical treated Fe-20Mn-12Cr-3Ni-3Si alloy. αʹ and ε-martensite were formed by deformation and thermo-mechanical treatment. With the increasing cycle number of thermo-mechanical treatment, volume fraction of ε-martensite was increased, and then decreased, whereas dislocation and αʹ-martensite were slowly increased. In 5-cycle number thermo-mechanical treated specimens result showed more than 10% of the volume fraction of ε-martensite and less than 3% of the volume fraction of αʹ-martensite. With the increasing number of thermo-mechanical treatment, the strength rapidly increased, but the damping capacity was slowly decreased, and results of damping capacity was the opposite to tendency for a metal with deformation induced martensite transformation. The damping capacity was decreased with the strength increasing, these results was opposite to tendency for metal with deformation induced martensite transformation. The strength was affected to formation of martensite and dislocation, grain refining by thermo-mechanical treatment, damping capacity was affected formation of dislocation and grain refinement.
- Author(s)
- 오동석
- Issued Date
- 2019
- Awarded Date
- 2019. 8
- Type
- Dissertation
- Publisher
- 부경대학교
- URI
- https://repository.pknu.ac.kr:8443/handle/2021.oak/23509
http://pknu.dcollection.net/common/orgView/200000221363
- Affiliation
- 부경대학교 산업대학원
- Department
- 산업대학원 금속공학과
- Advisor
- 강창룡
- Table Of Contents
- 제Ⅰ장 서론 1
제Ⅱ 장 이론적 배경 4
1. 마르텐사이트 변태의 특징 5
2. 역변태 오스테나이트 11
3. 진동감쇠 기구 11
4. 진동감쇠능의 측정 22
제Ⅲ 장 실 험 방 법 28
1. 시료 29
2. 가공열처리 29
3. 미세조직 관찰 29
4. 감쇠능 측정 30
5. 인장강도 측정 30
제Ⅳ 장 실험결과 및 고찰 31
1. 미세조직 관찰 32
2. 가공열처리에 따른 미세조직 변화 38
3. 기계적 성질과 감쇠능의 상호관계 44
제Ⅴ 장 결론 50
참고문헌 52
- Degree
- Master
-
Appears in Collections:
- 산업대학원 > 금속공학과
- Authorize & License
-
- Files in This Item:
-
Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.