Abstract: The purpose of this research is improve the mechanical properties and develop manufacturing technology through self-soluble alloy powder flame spray coating on the surface of the run-out table roller for hot rolling. The roller surface of the run-out table should maintain high hardness at high temperature and improve wear, corrosion, heat, adhesion resistance. In addition, the adhesive strength that does not peel off the coating layer by increasing the bonding strength between the thermal spray coating layer and the base material is also an important factor. In this study, it was possible to find the most suitable powder and process for roll manufacturing technology through initial selection of commercial alloy powder for roll manufacturing, hardness, component analysis, and adhesive strength analysis of the powder and thermal spray coating layer according to the powder.

URI: https://repository.pknu.ac.kr:8443/handle/2021.oak/24334
http://pknu.dcollection.net/common/orgView/200000600743

Table Of Contents: Ⅰ. 서 론 1
Ⅱ. 이론적 배경 5
2.1. 용사의 역사 및 현황 5
2.2. 용사의 종류 6
2.3. 용사의 특징 8
2.3.1. 고온/고속가스의 유동 8
2.3.2. 용융 입자의 가속 및 가열속도 9
2.3.3. 용융 입자의 충돌 변형 10
2.3.4. 코팅층의 미세구조와 물성 15
2.4. 용사 재료 17
2.5. 용사 기술의 활용도와 제품적용 19

Ⅲ. 실험방법 20
3.1. 상용 분말 20
3.2. 분말 형상 입형 및 성분 분석 21
3.3. 합금 분말 경도 시편 제작 21
3.4. 합금 분말 경도 특성 파악 21
3.5. Powder flame spray 공정을 이용한 용사 시편 제작 22
3.5.1. 용사 작업 조건 선정 22
3.5.2. 용사 시편 제작 22
3.5.3. 용사 표면층 경도 측정 22
3.5.4. 최적화 조건 선정 23
3.6. 용사 시편 접합강도 측정 25
3.7. 충돌해석 시험 26
Ⅳ. 실험 결과 27
4.1. 분말 합금 특성 27
4.1.1. SEM 결과 27
4.1.2. EDX 결과 39
4.2. 합금 분말 경도 시험 35
4.3. 용사 작업조건 선정 37
4.4. 용사 시편 경도 측정 42
4.5. 용사 작업조건에 대한 경도 측정 43
4.6. 용사 층 접합강도 측정 44
4.7. 용사 건 거리에 따른 충돌해석시험 46
Ⅴ. 결론 49