혼합가스와 공기 중에서 공업용 순 티타늄의 고온산화 거동
- Alternative Title
- High Temperature Oxidation Behavior of Commercial Pure Titanium in Mixed Gas and Air
- Abstract
- The oxidation behavior of commercial pure titanium has been investigated in the temperature range of 727℃ to 950℃ for 30min to 240min in mixed gas and Air.
The weight changes were measured by using TGA during oxidation in mixed gas and Air. The oxidation behavior indicated by weight gain or the growth of oxide thickness was based on the parabolic rule. The structures of the oxide scales formed during oxidation were analysed by using optical microscope, electron probe microanalyses, scanning electron microscope and x-ray measurements. The formation of oxide scale was influenced by the oxidation temperature, time and the condition of atmosphere. The scales have a rutile(TiO₂) structure, and are consisted of two layers of a porous external and a dense internal one.
- Issued Date
- 2007
- Awarded Date
- 2007. 8
- Type
- Dissertation
- Publisher
- 부경대학교 대학원
- Alternative Author(s)
- Park, Sung-Ho
- Affiliation
- 부경대학교 대학원
- Department
- 대학원 재료공학과
- Advisor
- 안용식
- Table Of Contents
- 1. 서론 = 1
1.1 연구 배경 및 목적 = 1
2. 이론적 배경 = 3
2.1 티타늄의 특성 = 3
2.2 티타늄의 산화 = 4
2.3 고온 산화 기구 = 7
2.3.1 Wagner의 고온 산화 속도론 = 7
2.4 산화막의 성장과 응력 발달 = 15
2.4.1 산화막 성장 메카니즘 = 15
2.4.2 성장 응력(Growth stress) = 18
2.4.3 열응력(Thermal stress) = 20
2.4.4 응력 완화 = 21
3. 실험 방법 = 24
3.1 실험 재료 = 24
3.2 고온 사화 장치 구성 = 24
3.3 고온 산화 속도 측정 = 25
3.4 미세 조직 관찰 및 분석 = 25
4. 실험 결과 및 고찰 = 28
4.1 산화 스케일의 형태와 특징 = 28
4.2 산화 온도에 따른 스케일 성장 거동 = 30
4.3 산화 시간에 따른 스케일 성장 거동 = 31
4.4 산화 분위기에 따른 스케일 성장 거동 = 32
4.5 산화 분위기에 따른 Ti-O 고용체 층의 거동 = 34
4.6 고온 산화에 따른 산화증량 = 36
4.7 고온 산화에 따른 결과 분석 = 37
5. 결론 = 44
6. 참고 문헌 = 45
감사의 글 = 48
- Degree
- Master
- Files in This Item:
-
-
Download
혼합가스와 공기 중에서 공업용 순 티타늄의 고온산화 거동.pdf
기타 데이터 / 4.72 MB / Adobe PDF
-
Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.