Al-Mg-Si계 주조용 합금의 조직미세화에 미치는 미량원소 첨가의 영향
- Alternative Title
- Effects of Trace Elements on Grain Refinement of Al-Mg-Si Casting Alloys
- Abstract
- Effects of trace elements on grain refinement Al-4Mg-0.9Si casting alloys have been studied.
Refining effect of primary crystals increased with nucleation temperature of primary crystal higher. Modification effect of eutectics, morphological change to fibrous was prominent with growth temperature of eutectics decreased as trace elements of Sr and Sc were added. Maximum fluidity appeared at the addition condition for the most refined primary crystal, 0.15wt.% Ti.
Key point to the development of Al-Mg-Si casting alloy with high-elongation property is to reduce main casting defects(oxide inclusion, shrinkage pore) by enhancing melt cleanness and adapting good casting design.
- Issued Date
- 2011
- Awarded Date
- 2011. 2
- Type
- Dissertation
- Keyword
- 조직미세화 grain refiner eutectic modifier
- Publisher
- 부경대학교
- Affiliation
- 부경대학교 대학원
- Department
- 대학원 금속공학과
- Advisor
- 김헌주
- Table Of Contents
- 1. 서 론 2
2. 이론적 배경 4
2. 1. 결정립 미세화 4
2. 2. 공정 개량화 9
2. 3. Al의 주조성 13
3. 실험방법 20
3. 1. 시료제조 20
3. 2. 열분석 및 미세조직 관찰 22
3. 3. 주조성 평가 24
3. 4. 인장 특성 평가 27
4. 실험결과 및 고찰 29
4. 1. 열분석 결과 및 미세조직 관찰 29
4.1.1 미량원소 첨가에 따른 초정 미세화 영향 29
4.1.1 미량원소 첨가에 따른 공정 개량화 영향 34
4. 2. 미량원소 첨가에 따른 유동성 영향 40
4. 3. 미량원소 첨가에 따른 수축성 영향 42
4. 4. 미량원소 첨가에 따른 인장 특성 및 시효 열처리의 영향 44
5. 결 론 51
참 고 문 헌 53
- Degree
- Master
- Files in This Item:
-
-
Download
Al-Mg-Si계 주조용 합금의 조직미세화에 미치는 미량원소 첨가의 영향.pdf
기타 데이터 / 1.83 MB / Adobe PDF
-
Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.