Abstract: Abstract

Ultrasonic testing of austenite stainless steel welds have been many problems and difficulties to detect faults through ultrasonic testing due to course grain size at the room temperature. It is required to apply advanced nondestructive testing for austenite stainless steel welds because of traditional UT techniques have low reliability for detection and evaluation of weld defects.
This study is analyzed for property of ultrasonic and ultrasonic signal for detecting defect. The austenite stainless steel welds is measured ultrasonic velocity and attenuation coefficient, and detected the defect in the austenite stainless steel welds by ultrasonic signal. The attenuation coefficient in weld metal is higher than in base metal, ultrasonic velocity in weld metal is lower than in base metal. therefore attenuation coefficient has an inverse proportion to ultrasonic velocity.

URI: https://repository.pknu.ac.kr:8443/handle/2021.oak/9586
http://pknu.dcollection.net/jsp/common/DcLoOrgPer.jsp?sItemId=000001963841

Table Of Contents: 목 차

Abstract

1. 서론 1

2. 이론적 배경 3
2.1 스테인리스강 3
2.1.1 스테인리스강의 정의 3
2.1.2 오스테나이트 스테인리스강 4
2.2 GMAW 용접 프로세스 5
2.2.1 GMAW 용접의 정의 5
2.2.2 GMAW 용접의 원리 6
2.2.3 GMAW 용접의 분류 7
2.3 초음파에 의한 시험 8
2.3.1 초음파 8
2.3.2 초음파 음속측정 10
2.3.3 초음파 감쇠계수 11
2.3.4 초음파 탐상시험 12
2.3.4.1 펄스 반사법(Pulse-echo method) 13
2.3.4.2 파동의 모드와 형상 14
2.3.4.3 초음파 탐상장치 17
2.3.4.4 탐촉자 19
2.3.4.5 표시 방식에 의한 분류 22

3. 실험 재료 및 실험 방법 23
3.1 실험재료 23
3.2 실험방법 24
3.2.1 GMAW 용접법 및 용접 조건 24
3.2.2 미세조직 및 결함 관찰 27
3.2.3 기계적 특성 시험 28
3.2.4 초음파 탐상 시험 29
3.2.4.1 초음파 전파속도 측정 31
3.2.4.2 초음파 감쇠계수 측정 32
3.2.4.3 초음파 신호 분석 33
3.2.5 방사선 투과 시험 35

4. 실험 결과 및 고찰 36
4.1 GMAW 비드 형상 관찰 36
4.2 미세 조직 관찰 38
4.3 기계적 특성 46
4.4 초음파 특성 평가 49
4.4.1 초음파 전파속도 측정 49
4.4.2 초음파 감쇠계수 측정 54
4.5 결함의 초음파 신호 분석 57
4.6 방사선 투과 시험 61

5. 결론 65

6. 참고문헌 66

감사의 글