WC-Ni계 초경합금의 기계적 성질에 미치는 첨가원소의 영향
- Alternative Title
- Effect of additive elements on the mechanical properties of WC-Ni hardmetal
- Abstract
- In the present study, the focus is the alalysis of the influences of B4C and TiH2 on the mechanical properties of WC-Ni hardmetal. The WC-Ni hardmetals were prepared by the combination of the mechanical milling and liquid phase sintering processes. The change in the microstructure, hardness and fracture toughness with the amount of the B4C and TiH2 were analyzed using SEM, Vickers hardness and three point bending test.
The sintered density of the WC-Ni hardmetal increased with addition of B4C with 0.3wt.%. The hardness of the WC-Ni hardmetal showed the tendency to increase as B4C content increased, however, the transverse rupture strength of one decreased with increasing addition of B4C.
The sinterability, hardness and transverse rupture strength of the WC-Ni hardmetal decreased with increasing addition of TiH2.
- Issued Date
- 2011
- Awarded Date
- 2011. 2
- Type
- Dissertation
- Publisher
- 부경대학교
- Alternative Author(s)
- Kang, Tea Hoon
- Affiliation
- 부경대학교 대학원
- Department
- 대학원 소재프로세스공학과
- Advisor
- 이길근
- Table Of Contents
- 1. 서 론 1
2. 이론적 배경 3
2.1 초경합금 3
2.1.1 초경합금의 정의 및 연구개발 동향 3
2.1.2 초경합금의 제조 7
2.1.3 초경합금의 결합금속 11
2.1.4 첨가원소 12
2.2 액상소결 12
3. 실험 방법 27
3.1 WC-Ni계 혼합 분말의 제조 및 성형 27
3.2 WC-Ni계 혼합 분말의 소결 27
3.3 WC-Ni계 혼합 분말과 소결체의 특성평가 31
4. 결과 및 고찰 33
4.1 WC-Ni-Si계 초경합금에 미치는 B4C의 영향 33
4.1.1 Ni-Si-B4C계 결합금속의 상호반응 33
4.1.2 치밀화에 미치는 B4C의 영향 37
4.1.3 기계적 성질에 미치는 B4C의 영향 42
4.2 WC-Ni-Si-B4C계 초경합금에 미치는 TiH2의 영향 51
4.2.1 Ni-Si-B4C-TiH2계 결합금속의 상호반응 51
4.2.2 치밀화에 미치는 TiH2의 영향 52
4.2.3 기계적 성질에 미치는 TiH2의 영향 56
5. 결 론 61
6. 참고문헌 62
- Degree
- Master
- Files in This Item:
-
-
Download
WC-Ni계 초경합금의 기계적 성질에 미치는 첨가원소의 영향.pdf
기타 데이터 / 1.38 MB / Adobe PDF
-
Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.